Colorant including a mixture of pigments

ABSTRACT

A colorant including a mixture of pigments is disclosed. The pigments have a similar coloration but different resistance to corrosion. The mixing ratio is selected to optimize the corrosion resistance against color brightness, and/or acidic corrosion resistance against alkali corrosion resistance of the colorant.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. patent application Ser. No. 14/043,497, filed Oct. 1, 2013 (now U.S. Pat. No. 9,796,856), which claims priority from U.S. Provisional Patent Application No. 61/708,479, filed Oct. 1, 2012, the disclosures of which are incorporated herein by reference.

TECHNICAL FIELD

The present invention relates to colorants, and in particular to improving corrosion resistance of colorants.

BACKGROUND OF THE INVENTION

Blending of pigments has a long history, 32,000 years ago prehistoric artist used blends of ground red or yellow ochre with clays, charcoal, juice of berries and fat for making paintings on cave walls and ceilings. Currently, blending of various pigments takes place in many industries and in fine arts. Main purpose of blending of pigments is mixing of pigments with different color to get another, composite color. The blending is brought to a level of high sophistication, with a considerable control of the color properties of the final products.

For industrial applications, as well as in fine arts, permanence and stability of inorganic, organic, or special pigments and their blends are highly desirable. Such attributes as heat stability, toxicity, tinting strength, staining, dispersion, opacity or transparency, resistance to alkaline or acid, interaction between pigments as well as lightfastness (resistance to discoloration caused by light exposure), determine their suitability for particular manufacturing processes and applications. Chemical or electrochemical degradation of pigments typically cause economical losses.

Various methods have been used in the industry to strengthen the corrosion resistance of pigments, including deposition of protective coatings on the top of pigment particles, and/or addition of passivators and corrosion inhibitors to the ink or paint vehicle. For example, Li et al. in US Patent Application Publication 2008/0314284 disclose highly anti-corrosive thin platelet-like metal pigments, in which the surface of thin platelet-like metal substrates are treated with phosphoric acid compounds and/or boric acid compounds, and are further coated with a layer containing hydrated tin oxide to improve the corrosion resistance. Detrimentally, the passivated pigments of Li et al. are more costly than their non-passivated counterparts, due to additional labor and materials costs.

Goniochromatic optical interference pigments, also termed as color-shifting interference pigments, provide bright, vivid colors due to their multilayered interference structure. Optical interference pigments containing a metallic reflector layer and one or more semi-transparent absorber layers are most color-effective among all known high performance pigments. However, these pigments are highly sensitive to the exposure of corrosive media.

Protective coatings can be applied to color-shifting interference pigments. For example, Phillips in US Patent Application Publication 2004/0160672 disclose color-shifting multilayer interference pigments with the outer layers of silicone dioxide that function as a protective layer for the core optical structure C/SiO₂/C. In a paint or ink composition that may be subjected to abrasion in a delivery system, the SiO₂ outer layers are known to prevent abrasion to the core optical structure that gives rise to color. Thus, in this instance, the color in the paint or ink composition is more durable. Vuarnoz et al. in U.S. Pat. No. 7,381,758 disclose a passivated optically variable pigment, and suitable passivating compounds for this pigment, including anionic tensides.

Corrosion resistance of goniochromatic interference pigments can also be improved by heat treatment of pigment particles. For example, Phillips et al. in U.S. Pat. No. 5,569,535 disclose a collection of color-shifting interference thin film platelets of high chroma. In order to impart additional durability to the interference platelets, the latter can be annealed or heat treated at a temperature ranging from 200° C.-300° C., and preferably from 250° C.-275° C., for a period of time ranging from 10 minutes to 24 hours, and preferably a time of approximately 15-30 minutes.

Phillips et al. in U.S. Pat. No. 5,570,847 and US Patent Application Publication 2002/0160194; and Bradley et al. in U.S. Pat. Nos. 6,157,489; 6,243,204; and 6,246,523 disclose a method of heat-treating multilayer interference platelets to improve durability of the platelets, including subjecting the platelets at a temperature of 200° C.-300° C. for 10 minutes to 24 hours. The platelets are formed from a multilayer color-shifting interference thin film construction comprising a metal reflecting layer having a multilayer interference thin film structure on both sides of the metal reflecting layer. The multilayer interference thin film structure includes a pair of layers consisting of a dielectric layer and a semi-opaque metal layer with the dielectric layer of the pair being directly adjacent to the metal reflecting layer. However, the pigments of Phillips et al. and Bradley et al. require the extra step of heat treatment at elevated temperatures.

SUMMARY OF THE INVENTION

Corrosion resistance of many pigments decreases with an increase of color brightness. In other words, pigments of a vivid luminous color are frequently prone to corrosion-induced degradation more than pigments of a same, but somewhat more dull color. The inventors have discovered that by mixing together two pigments of similar color but a slightly different chroma or lightness of the color, a colorant can be obtained that has sufficiently vivid colors, and at the same time is sufficiently resistant to corrosion.

For instance, a color-shifting interference pigment including an aluminum reflector produces more vivid colors than a color-shifting interference pigment of a similar color, but based on a chromium reflector, because aluminum is more reflective than chromium. However, aluminum is known to degrade relatively quickly in alkaline solutions, whereas chromium is more stable in such solutions; and chromium degrades in an acidic environment while aluminum is stable in the acidic environment. Therefore, by mixing together aluminum-based and chromium-based interference pigments of a same or similar color, a sufficiently stable and bright colorant may be obtained that is more corrosion resistant than aluminum in alkaline solutions and chromium in acidic solutions.

Many pigments fall into one of two categories. Pigments of a first category show good resistance to acidic environments, but are prone to degradation in alkaline environments. Pigments of a second category are resistant to alkaline environments, but degrade in acidic environments. The inventors have discovered that blending two pigments belonging to these different categories, but exhibiting similar or even exactly the same color, can result in increasing an overall chemical durability of the blend in both acidic and alkaline solutions, as compared to the most sensitive individual pigments of the blend. This finding is particularly valuable for optical interference pigments, because their color characteristics can be generally decoupled from the material system used. As a result, mixing two pigments of a substantially same hue or chroma, but different material systems falling into different corrosion resistivity categories can result in a pigment generally durable in multiple corrosive environments. Thus, mixing pigments of a substantially same color, while appearing unnecessary in view of prior-art mixing of pigments of different colors to obtain new colors, provides significant advantages for improving corrosion resistance.

In accordance with the invention, there is provided a colorant comprising a mixture of first pigment P₁ and second pigment P₂ having chroma C*₁ and C*₂, respectively, wherein each of C*₁ and C*₂ is at least 10 units in CIE 1976 L*a*b* color space—hereinafter referred to as the L*a*b* color space—under illumination by a D65 standard light source using the 10 degree observer function, wherein s color difference Δhue between the first and second pigments is no more than 30 hue degrees;

wherein the first pigment undergoes a corrosion-induced color change ΔE*(P₁) when immersed into a corrosive solution, and wherein the second pigment undergoes a corrosion-induced color change ΔE*(P₂) when immersed into the corrosive solution, wherein ΔE*(P₂)<ΔE*(P₁),

whereby a corrosion-induced color change ΔE*(P₁+P₂) of the colorant upon immersion into the corrosive solution satisfies the condition ΔE*(P₁+P₂)<ΔE*(P₁),

wherein the corrosive solution is selected from the group consisting of 2% by weight aqueous solution of H₂SO₄, 2% by weight aqueous solution of NaOH, 1.2% by weight aqueous solution of sodium hypochlorite bleach, and water.

In accordance with a preferred embodiment of the invention, when the first pigment corrodes more in basic solutions than in acidic solutions, that is, ΔE*_(B)(P₁)>ΔE*_(A)(P₁); the second pigment corrodes more in acidic solutions than in basic solutions, that is, ΔE*_(A)(P₂)>ΔE*_(B)(P₂); and the second pigment corrodes more in acid that the first, that is, ΔE*_(A)(P₂)>ΔE*_(A)(P₁), the mixture of the first and second pigments can be more stable in acidic solutions than the second pigment alone, that is, ΔE*_(A)(P₁+P₂)<ΔE*_(A)(P₂); while being more stable in basic (alkali) solutions than the first pigment alone, that is, ΔE*_(B)(P₁+P₂)<ΔE*_(B)(P₁). This allows one to mix two pigments of a similar or even exactly the same color, while meeting the specifications for both the acidic and alkali resistance simultaneously; and, of course, meeting the specification for the targeted color.

In accordance with the invention, there is further provided a method of manufacture of a colorant, the method comprising:

(a) providing a first pigment P₁ and second pigment P₂ each having chroma C*₁ and C*₂, respectively, wherein each of C*₁ and C*₂ is at least 10 units in L*a*b* color space under illumination by a D65 standard light source using the 10 degree observer function, wherein a color difference between the first and second pigments is no more than 30 hue degrees in the polar projection of the L*a*b* color space, wherein the first pigment undergoes a corrosion-induced color change ΔE*(P₁) upon immersion into a corrosive solution, and wherein the second pigment undergoes a corrosion-induced color change ΔE*(P₂) upon immersion into the corrosive solution, wherein ΔE*(P₂)<ΔE*(P₁); and

(b) mixing together the first and second pigments to obtain the colorant having a corrosion-induced color change ΔE*(P₁+P₂) upon immersion into the corrosive solution satisfying the ΔE*(P₁+P₂)<ΔE*(P₁),

wherein the corrosive solution is selected from the group consisting of 2% by weight aqueous solution of H₂SO₄, 2% by weight aqueous solution of NaOH, 1.2% by weight aqueous solution of sodium hypochlorite bleach, and water. These percentages are of course exemplary and are introduced for clarity. Other concentrations can be used to the same effect.

In one embodiment, in step (a), the corrosion-induced color changes of the first and second pigments and the colorant comprise base-induced color changes ΔE*_(B)(P₁), ΔE*_(B)(P₂), and ΔE*_(B)(P₁+P₂), respectively, upon immersion into the 2% by weight aqueous solution of NaOH.

Furthermore, in one embodiment, in step (a), the first pigment undergoes an acid-induced color change ΔE*_(A)(P₁) upon immersion into the 2% by weight aqueous solution of H₂SO₄, wherein ΔE*_(A)(P₁)<ΔE*_(B)(P₁); and the second pigment undergoes an acid-induced color change ΔE*_(A)(P₂) upon immersion into the 2% by weight aqueous solution of H₂SO₄, wherein ΔE*_(A)(P₂)>ΔE*_(B)(P₂). When ΔE*_(A)(P₂)>ΔE*_(A)(P₁), an acid-induced color change ΔE*_(A)(P₁+P₂) of the colorant upon immersion into the 2% by weight aqueous solution of H₂SO₄ satisfies the condition ΔE*_(A)(P₁+P₂)<ΔE*_(A)(P₂).

Three or more pigments can be mixed to make a corrosion-resistant colorant. The conditions disclosed herein for two-component blends also apply to the case of three-component blends and multi-component blends. For three-component compositions, each component proportion in the colorant is preferably at least 25% by weight.

BRIEF DESCRIPTION OF THE DRAWINGS

Exemplary embodiments will now be described in conjunction with the drawings, in which:

FIGS. 1A and 1B are diagrams of a colorant (FIG. 1B) obtained by mixing two different pigments (FIG. 1A);

FIG. 2 is a diagram of a corrosion-induced color change of the two pigments of FIG. 1A and the colorant of FIG. 1B;

FIG. 3 is a three-dimensional view of a color-shifting interference pigment chip of one embodiment of the first pigment of FIG. 1A;

FIG. 4 is a diagram of a base-induced color change of the two color-shifting interference pigments of FIG. 1A and the mixture of these pigments shown in FIG. 1B;

FIG. 5 is a process window diagram for mixing the first and second pigments of FIG. 1A to obtain a colorant of FIG. 1B having an improved alkali resistance, such as the one illustrated by the color change diagram of FIG. 4;

FIG. 6 is a diagram of an acid-induced color change of the two pigments of FIG. 1A and the colorant of FIG. 1B;

FIG. 7 is a combination of the diagrams of FIGS. 4 and 6; and

FIG. 8 is a process window diagram for mixing the first and second pigments of FIG. 1A to obtain a colorant having improved alkali and acidic resistance, such as the one illustrated by the color change diagram of FIG. 7.

DETAILED DESCRIPTION OF THE INVENTION

While the present teachings are described in conjunction with various embodiments and examples, it is not intended that the present teachings be limited to such embodiments. On the contrary, the present teachings encompass various alternatives and equivalents, as will be appreciated by those of skill in the art.

Referring to FIGS. 1A and 1B, an exemplary colorant 10 is obtained by mixing first 11 and second 12 pigments P₁ and P₂ in a vial 19. The first 11 and second 12 pigments P₁ and P₂ have chroma parameters C*₁ and C*₂, respectively. Each of C*₁ and C*₂ is at least 10 unites in L*a*b* color space under illumination by a D65 standard light source using the 10 degree observer function. Although other chroma definitions can be used, the above definition has been selected for certainty of the chroma definition. The chroma parameters C*₁ and C*₂ of at least 15 units are preferable, because they result in brighter pigments. More preferably, the parameters C*₁ and C*₂ are at least 25 units.

According to the invention, the first 11 and second 12 pigments being mixed together are of a same or similar color. Quantitatively, this can be expressed via a color difference Δhue between the first and second pigments, which is no more than 30 hue degrees, preferably no more than 20 hue degrees and more preferably no more than 15 hue degrees in the polar projection of the aforementioned L*a*b* color space using the same observer function.

The corrosion resistivity of the pigments 11 and 12 can be represented by a color change exhibited when the pigments 11 and 12 are immersed into a standardized corrosive medium, including alkaline acidic solutions, a bleach solution, or water. It is assumed that the first pigment 11 undergoes a corrosion-induced color change ΔE*(P₁) when immersed into a corrosive solution, and the second pigment 12 undergoes a corrosion-induced color change ΔE*(P₂) when immersed into the corrosive solution.

Turning to FIG. 2, the corrosion-induced color change ΔE*(P₂) of the second pigment 12, shown with a bottom solid line 22, is less than the corrosion-induced color change ΔE*(P₁) of the first pigment 11, shown with a top solid line 21. The colorant 10 is a mixture of the pigments 11 (P₁) and 12 (P₂). Since ΔE*(P₂)<ΔE*(P₁), a corrosion-induced color change ΔE*(P₁+P₂) upon immersing the colorant 10 into the corrosive solution will generally be less than ΔE*(P₁), which is the largest ΔE* of the two pigments 11 and 12. The corrosion-induced color change ΔE*(P₁+P₂) of the colorant 10 is shown in FIG. 2 with a dashed line 20 disposed between the solid lines 21 and 22. The rationale to mix the less stable first pigment 11 into the more stable pigment 12 is to meet particular color brightness or vividness characteristics. For example, when chroma C*₁ of the first pigment 11 is higher than the chroma C*₂ of the second pigment 12, the chroma C* of the mixture colorant 10 will be generally higher than the chroma C*₂ of the second pigment 12.

The corrosive solution can include 2% by weight aqueous solution of H₂SO₄, 2% by weight aqueous solution of NaOH, a 1.2% by weight aqueous solution of sodium hypochlorite bleach, or distilled water. The corrosion-induced color change ΔE* is calculated using the formula ΔE*=√{square root over ((ΔL*)²+(Δa*)²+(Δb*)²)}  (1)

wherein ΔL* is the lightness change, and Δa* and Δb* are color coordinate changes in the L*a*b* color space, caused by corrosion.

In a preferred embodiment of the invention, the first 11 and second 12 pigments include color-shifting pigments, which are formed from a multilayer thin film structure broken down into small flakes. The multilayer film structure includes an absorber layer or layers, a dielectric layer or layers, and optionally a reflector layer, in varying layer orders. The coatings can be formed to have a symmetrical multilayer thin film structure, such as absorber/dielectric/reflector/dielectric/absorber; or absorber/dielectric/absorber. Coatings can also be formed to have an asymmetrical multilayer thin film structure, such as absorber/dielectric/reflector. Color-shifting multilayer interference pigments are particularly advantageous in this invention, because for these pigments, the color can be decoupled, from the material system used, allowing one to vary the materials of the dielectric, semi-transparent, and reflective layers to fulfill certain corrosion resistance criteria, while varying thicknesses of these materials to match to each other colors of individual pigments.

By way of a non-limiting illustrative example shown in FIG. 3 with further reference to FIGS. 1A and 1B, the first pigment 11 can include a plurality of color-shifting interference flakes 30 (FIG. 3) including in sequence a top semi-transparent chromium (Cr) layer 31, a top dielectric magnesium fluoride (MgF₂) layer 32, a reflective opaque aluminum (Al) layer 33, a bottom dielectric magnesium fluoride (MgF₂) layer 34, and a bottom semi-transparent chromium (Cr) layer 35. Of course, the terms “top” and “bottom” are relative, since the flakes 30 can have any orientation when suspended within the first pigment 11. The thicknesses of the first and second chromium 31, 35 and MgF₂ layers 32, 24 are selected to make the pigment 11 have blue-greenish color. The second pigment 12 includes the same basic structure of the flakes 30, only the dielectric layers 32, 34 are made of silicon dioxide (SiO₂), and the center reflector layer 33 includes chromium which is effectively opaque. The first 11 and second 12 pigments of this composition have chroma of at least 10 units in L*a*b* color space under illumination by a D65 standard light source using the 10 degree observer function, as measured using a standard d/8° integrating sphere geometry. The color difference Δhue between the first 11 and second 12 pigments is no more than 30 hue degrees in the polar projection of the L*a*b* color space at the above illumination/observation conditions.

Table 1 below shows results of testing of color degradation of the first 11 and second 12 pigments upon immersion into 2% by weight aqueous solution of NaOH. The values of C* were measured before the immersion. Δhue₁₁₋₁₂ is a difference of hue between the pigments 11 and 12.

TABLE 1 Sample Pigment ΔE*_(B) C* Δhue₁₁₋₁₂ Pigment 11: green-to-blue Cr/MgF₂/Al/MgF₂/Cr 27.04 60.70 Pigment 12: green-to-blue Cr/SiO₂/Cr/SiO₂/Cr 4.05 52.30 50:50 mixture of Pigments 11 and 12 12.47 56.05 6.06°

Mixing together the color-shifting interference pigments 11 and 12 of Table 1 at different ratios allows one to optimize the color brightness (chroma) performance of the resulting colorant 10, as well as bring the base-induced color change ΔE*_(B)(P₁+P₂) of the colorant 10 below a pre-defined level. Referring to FIG. 5, chroma C* and the base-induced color change ΔE*_(B) of the colorant 10 are plotted as a function of P₂/P₁ mixing ratio. A top solid line 51 represents chroma C*(P₂/P₁) dependence, and a bottom solid line 52 represents the base-induced color change ΔE*_(B)(P₁+P₂). In this example, the mixing ratio P₂/P₁ is selected to simultaneously fulfill two criteria: to have the chroma C* above a threshold value C*₀, and to have the base-induced color change ΔE*_(B) below a threshold value ΔE*₀.

The chroma line 51 shows that as the ratio P₂/P₁ increases, the chroma C* decreases. This is because the chromium reflective layer 33 of the chips 30 of the second pigment 12 is not as reflective as the corresponding aluminum reflective layer 33 of the first pigment 11. A shaded area 53 above the threshold chroma value C*₀ denotes a range of acceptable mixing ratios P₂/P₁, at which chroma C*>C*₀.

The color change line 52 shows that as the mixing ratio P₂/P₁ increases, the color change also decreases. This is because the chromium reflective layer 33 of the chips 30 of the second pigment 12 is more stable in basic (alkali) solutions than the corresponding aluminum reflective layer of the first pigment 11. A shaded area 54 below the threshold color change value ΔE*₀ denotes a range of acceptable mixing ratios P₂/P₁, at which chroma ΔE*_(B)<ΔE*₀.

Together, the shaded areas 53 and 54 define a process window 55 having a range 56 of acceptable mixing ratios P₂/P₁, which satisfy the conditions C*>C*₀ and ΔE*_(B)<ΔE*₀ simultaneously. It has been found that a range of mixing ratios P₂/P₁ varying between 25:75 and 75:25 by weight can provide practically useful results.

Turning to FIG. 6, acid-induced color change of the first pigment 11 ΔE*_(A)(P₁) is shown with a bottom dotted line 61, and the acid-induced color change of the second pigment 12 ΔE*_(A)(P₂) is shown with a top dotted line 62. The acid-induced color change ΔE*_(A)(P₁+P₂) upon immersing the colorant 10 into the 2% by weight aqueous solution of H₂SO₄ is less than ΔE*_(A)(P₂). The acid-induced color change ΔE*_(A)(P₁+P₂) is shown with a dotted-dashed line 60. In a preferred embodiment of the invention, the two pigments 11 and 12 are selected so that while the first pigment 11 corrodes more in basic solutions than in acidic solutions, that is, ΔE*_(B)(P₁)>ΔE*_(A)(P₁), the second pigment 12 corrodes more in acidic solutions than in basic solutions, that is, ΔE*_(A)(P₂)>ΔE*_(B)(P₂).

Referring to FIG. 7, the ΔE*_(B)(P₁)>ΔE*_(A)(P₁) and ΔE*_(A)(P₂)>ΔE*_(B)(P₂) conditions are illustrated by means of a corrosion-induced color change diagram. FIG. 7 is a combination of FIG. 4 showing the condition ΔE*_(B)(P₁)>ΔE*_(A)(P₁), and FIG. 6 showing the condition ΔE*_(A)(P₂)>ΔE*_(B)(P₂). Table 2 below includes results of corrosion-induced color degradation ΔE* testing for the material systems of the first 11 and second 12 pigments satisfying the ΔE* relationships represented by FIG. 7. In Table 2 below, the first 11 and second 12 pigments are color-shifting interference pigments including pigment flakes similar to the flake 30 shown in FIG. 3. The first pigment 11 includes the semi-transparent chromium (Cr) layers 31 and 35, the dielectric magnesium fluoride (MgF₂) layers 32 and 34, and the reflective aluminum (Al) layer 33. The second pigment 12 includes the semi-transparent bismuth (Bi) layers 31 and 35, the dielectric magnesium fluoride (MgF₂) layers 32 and 34, and the reflective ferrochrome (FeCr) layer 33. The first 11 and second 12 pigments of this composition have chroma of at least 10 units in L*a*b* color space under illumination by a D65 standard light source using the 10 degrees observer function, as measured using a d/8° integrating sphere geometry. The color difference ΔE* between the first 11 and second 12 pigments is no more than 30 hue degrees in the polar projection of the L*a*b* color space at the above illumination/observation conditions. The values of C* were measured before the immersion. Δhue₁₁₋₁₂ is a difference of hue between the pigments 11 and 12.

TABLE 2 Sample Pigment ΔE*_(B) ΔE*_(A) C* Δhue₁₁₋₁₂ Pigment 11: Cr/MgF₂/Al/MgF₂/Cr 27.04 1.79 60.70 Pigment 12: Bi/MgF₂/FeCr/MgF₂/Bi 4.71 30.12 37.25 50:50 mixture of Pigments 11 and 12 20.94 12.47 51.76 18.15°

Table 3 below illustrates corrosion performance of another material system. In Table 3, the first pigment 11 is the same as in Table 2. The second pigment 12 includes the semi-transparent iron (Fe) layers 31 and 35, the dielectric magnesium fluoride (MgF₂) layers 32 and 34, and the reflective ferrochrome (FeCr) layer 33. The first 11 and second 12 pigments of this composition have chroma of at least 10 units in L*a*b* color space under illumination by a D65 standard light source using the 10 degrees observer function, as measured using a d/8° integrating sphere geometry. The color difference between the first 11 and second 12 pigments is no more than 30 hue degrees in the polar projection of the L*a*b* color space at the above illumination/observation conditions.

TABLE 3 Sample Pigment ΔE*_(B) ΔE*_(A) C* Δhue₁₁₋₁₂ Pigment 11: Cr/MgF₂/Al/MgF₂/Cr 27.04 1.79 60.70 Pigment 12: Fe/MgF₂/FeCr/MgF₂/Fe 0.99 37.30 37.54 50:50 mixture of Pigments 11 and 12 14.30 7.35 49.53 27.12°

The positive-slope solid line 81 shows that as the ratio P₂/P₁ increases, the acid-induced color change ΔE*_(A)(P₂/P₁) of the mixture colorant 10 increases. This is because bismuth (Bi) is more sensitive to acids than to bases. A shaded area 83 below the threshold value ΔE*_(A0) denotes a range of acceptable mixing ratios P₂/P₁, at which chroma ΔE*_(A)(P₂/P₁)<ΔE*_(A0).

The negative-slope solid line 82 shows that as the ratio P₂/P₁ increases, the base-induced color change ΔE*_(B)(P₂/P₁) of the mixture colorant 10 decreases. This is because aluminum (Al) is more sensitive to bases than to acids. A shaded area 84 below the threshold value ΔE*_(B0) denotes a range of acceptable mixing ratios P₂/P₁, at which chroma ΔE*_(B)(P₂/P₁)<ΔE*_(B0).

Together, the shaded areas 83 and 84 define a process window 83 having a range 86 of acceptable mixing ratios P₂/P₁, which satisfy the conditions ΔE*_(A)(P₂/P₁)<ΔE*_(A0) and ΔE*_(B)(P₂/P₁)<ΔE*_(B0) simultaneously.

In accordance with a further embodiment of the invention, three or more pigments can be mixed together, for example, a third pigment P₃ having the semi-transparent chromium (Cr) layers 31 and 35, the dielectric silicon dioxide (SiO₂) layers 32 and 34, and the reflective chromium (Al) layer 33, can be added to the first 11 and second 12 pigments of Table 3 above. The third pigment P₃ based only on chromium and silicon dioxide is quite stable in both acidic and alkaline solutions but has a relatively low chroma. Accordingly, if the chroma specification permits, the third pigment P₃ added to the first and second pigments of Table 3, can further increase the corrosion resistance of the colorant 10, albeit at a slight drop of chroma C* of the colorant 10. To improve the corrosion resistance of the colorant 10, the corrosion-induced color change ΔE*(P₃) of the third pigment P₃ upon immersion into the corrosive solution should satisfy the condition ΔE*(P₃)<ΔE*(P₂). The chroma C*₃ of the third pigment P₃ should be at least 10 units in L*a*b* color space trader illumination by a D65 standard light source using a 10 degree observer function, and a color difference between the first P₁, second P₂, and third P₃ pigments is no more than 30 hue degrees in a polar projection of the L*a*b* color space. The three-component colorants 10 can include at least 25% of individual pigments P₁, P₂, and P₃ by weight.

A method of manufacture of the colorant 10 of the invention includes a first step of providing the first 11 (P₁) and second 12 (P₂) pigments, and a second step of mixing the pigments 11 and 12 together to obtain the colorant 10. The pigments 11 and 12 each have chroma C*₁ and C*₂, respectively, of at least 10 units in L*a*b* color space as explained above. The first pigment 11 undergoes a corrosion-induced color change ΔE*(P₁) upon immersion into a corrosive solution, and the second pigment 12 undergoes a corrosion-induced color change ΔE*(P₂) upon immersion into the corrosive solution, wherein ΔE*(P₂)<ΔE*(P₁). Upon mixing, the colorant 10 has ΔE*(P₁+P₂)<ΔE*(P₁) as explained above. The proportion of the first 11 and second 12 pigments in the colorant 10 is preferably between 25:75 and 75:25.

The corrosion-induced color changes of the first 11 and second 12 pigments and the colorant 10 include base-induced color changes ΔE*_(B)(P₁), ΔE*_(B)(P₂), and ΔE*_(B)(P₁+P₂), respectively, upon immersion into the 2% by weight aqueous solution of NaOH; and ΔE*_(A)(P₁), ΔE*_(A)(P₂), and ΔE*_(A)(P₁+P₂), respectively, upon immersion into the 2% by weight aqueous solution of H₂SO₄. In one embodiment, ΔE*_(A)(P₁)<ΔE*_(B)(P₁) and ΔE*_(A)(P₂)>ΔE*_(B)(P₂), while ΔE*_(A)(P₂)>ΔE*_(A)(P₁). This interrelationship between acidic and alkali induced color changes ΔE* of the ingredients result in acid-induced color change ΔE*_(A)(P₁+P₂) of the colorant 10 upon immersion into the 2% by weight aqueous solution of H₂SO₄ satisfying the condition ΔE*_(A)(P₁+P₂)<ΔE*_(A)(P₂), that is, the acidic resistance of the mixture colorant 10 improves as compared to that of the second pigment 12; and the alkali resistance of the mixture colorant 10 improves in comparison with that of the first pigment 11. The proportion of the first 11 and second 12 pigments in the colorant 10 is preferably between 25:75 and 75:25.

As noted above, the first 11 and second 12 pigments preferably include color-shifting interference pigments. For certainty, tire conditions of chroma C*₁ and C*₂ of at least 10 units in color space under illumination by a D65 standard light source using the 10 degree observer function, and the color difference between, the first 11 and second 12 pigments of no more than 30 hue degrees in the polar projection of the L*a*b* color space color space is fulfilled as measured using a d/8° integrating sphere geometry.

The chips or flakes 30 of the color-shifting interference pigments 11 and 12 can include, by means of example and without limitation, chromium (Cr), bismuth (Bi), iron (Fe), and ferrochrome (FeCr) outer semi-transparent layers 31 and 35, for providing different acid and/or alkali resistance. It is preferable that the first pigment 11 includes chromium (Cr) in the outer semi-transparent layers 31 and 35, and the second pigment 12 includes bismuth (Bi) or iron (Fe) in the outer semi-transparent layers 31 and 35. The reflective metal 33 can include aluminum (Al), chromium (Cr), ferrochrome (FeCr), and other materials.

The dielectric layers of the flakes 30 of the color-shifting interferometric pigments 11 and 12 can include layers having a “high” index of refraction, defined herein as greater than about 1.8 or 1.9, as well as those have a “low” index of refraction, which is defined herein as about 1.65 or less. Each of the dielectric layers 32, 34 (FIG. 3) can be formed of a single material or with a variety of material combinations and configurations. For example, the dielectric layers 32, 34 can be formed of only a low index material or only a high index material, a mixture or multiple sub-layers of two or more low index materials, a mixture or multiple sub-layers of two or more high index materials, or a mixture or multiple sub-layers of low index and high index materials. In addition, the dielectric layers can be formed partially or entirely of high/low dielectric optical stacks, which are discussed in further detail below. When a dielectric layer is formed partially with a dielectric optical stack, the remaining portion of the dielectric layer can be formed with a single material or various material combinations and configurations as described above.

Examples of suitable high refractive index materials for the dielectric layers 32, 34 include zinc sulfide (ZnS), zinc oxide (ZnO), zirconium oxide (ZrO₂), titanium dioxide (TiO₂) diamond-like carbon, indium oxide (In₂O₃), indium-tin-oxide (ITO), tantalum pentoxide (Ta₂O₅), ceric oxide (CeO₂), yttrium oxide (Y₂O₃), europium oxide (Eu₂O₃), iron oxides such as (II)diiron(III) oxide (Fe₃O₄) and ferric oxide (Fe₂O₃), hafnium nitride (HfN), hafnium carbide (HfC), hafnium oxide (HfO2), lanthanum oxide (La₂O₃), magnesium oxide (MgO), neodymium oxide (Nd₂O₃), praseodymium oxide (Pr₆O₁₁), samarium oxide (Sm₂O₃), antimony trioxide (Sb₂O₃), silicon monoxide (SiO), selenium trioxide (Se₂O₃), tin oxide (SnO₂), tungsten trioxide (WO₃), combinations thereof, and the like.

Examples of suitable low refractive index materials for the dielectric layers 32, 34 include silicon dioxide (SiO₂), aluminum oxide (Al₂O₃), metal fluorides such as magnesium fluoride (MgF₂), aluminum fluoride (AlF₃), cerium fluoride (CeF₃), lanthanum fluoride (LaF₃), sodium aluminum fluorides (e.g., Na₃AlF₆ or Na₅Al₃F₁₄), neodymium fluoride (NdF₃), samarium fluoride (SmF₃), barium fluoride (BaF₂), calcium fluoride (CaF₂), lithium fluoride (LiF), combinations thereof, or any other low index material having an index of refraction of about 1.65 or less. For example, organic monomers and polymers can be utilized as low index materials, including dienes or alkenes such as acrylates (e.g., methacrylate), perfluoroalkenes, polytetrafluoroethylene (Teflon), fluorinated ethylene propylene (FEP), combinations thereof and the like.

The foregoing description of one or more embodiments of the invention has been presented for the purposes of illustration and description. It is not intended to be exhaustive or to limit the invention to the precise form disclosed. Many modifications and variations are possible in light of the above teaching. It is intended that the scope of the invention be limited not by this detailed description, but rather by the claims appended hereto. For instance, the invention is not limited to color-shifting interference pigments. Other pigments such as interference pigments, lamellar pigments, mica pigments, metallic flake pigments, and organic pigments exhibiting different alkali and/or acidic and/or bleach and/or water resistance can be used as well. 

What is claimed is:
 1. A colorant comprising: a first pigment; and a second pigment, wherein the second pigment comprises a plurality of layers, wherein the plurality of layers include a particular layer, and wherein the particular layer is a reflective ferrochrome (FeCr) layer.
 2. The colorant of claim 1, wherein the particular layer includes chromium.
 3. The colorant of claim 1, wherein the first pigment includes a plurality of color-shifting interference flakes.
 4. The colorant of claim 1, wherein the first pigment includes a dielectric magnesium fluoride (MgF₂) layer.
 5. The colorant of claim 1, wherein the first pigment includes a reflective opaque aluminum (Al) layer.
 6. The colorant of claim 1, wherein the first pigment includes one or more semi-transparent chromium (Cr) layers.
 7. The colorant of claim 1, wherein the particular layer is between two or more other layers of the plurality of layers.
 8. The colorant of claim 1, wherein the plurality of layers further include silicon dioxide (SiO₂) dielectric layers.
 9. The colorant of claim 1, wherein the first pigment and the second pigment have a chroma of at least 10 units in an L*a*b* color space.
 10. The colorant of claim 1, wherein a color difference hue between the first pigment and the second pigment is no more than 30 hue degrees in a polar projection of an L*a*b* color space.
 11. A colorant comprising: a pigment, wherein the pigment comprises a plurality of layers, wherein the plurality of layers include a particular layer between two other layers of the plurality of layers, and wherein the particular layer is a reflective ferrochrome (FeCr) layer.
 12. The colorant of claim 11, further comprising: another pigment that includes a plurality of chromium (Cr) layers.
 13. The colorant of claim 11, further comprising: another pigment that includes an aluminum (Al) layer between four other layers.
 14. The colorant of claim 11, further comprising: another pigment that includes a dielectric magnesium fluoride (MgF₂) layer and a chromium (Cr) layer.
 15. The colorant of claim 11, where the two other layers include dielectric magnesium fluoride (MgF₂) layers.
 16. The colorant of claim 11, where the two other layers include semi-transparent bismuth (Bi) layers.
 17. The colorant of claim 11, where the two other layers include semi-transparent iron (Fe) layers.
 18. The colorant of claim 11, wherein the pigment is a first pigment, and wherein the colorant is a mixture of the first pigment and a second pigment.
 19. The colorant of claim 18, wherein a color difference hue between the first pigment and the second pigment is no more than 30 hue degrees in a polar projection of an L*a*b* color space.
 20. The colorant of claim 18, wherein the first pigment exhibits a higher color change ΔE*B in a basic solution than the second pigment, and wherein the second pigment exhibits a higher color change ΔE*A in an acidic solution than the first pigment. 